文章信息/Info

Title:
Analysis of corrosion causes of lubricating oil refining device
文章编号:
16742869(2012)04000605
作者:
唐丽娜1; 2;   游碧龙3; 刘毅3;  程健1; 2*; 袁军1; 2
1.武汉工程大学湖北省新型反应器与绿色化学工艺重点实验室，湖北 武汉430074；
2.武汉工程大学绿色化工过程省部共建教育部重点实验室，湖北 武汉 430074；
3.中国石化集团荆门分公司，湖北 荆门 448000
Author(s):
TANG Li\|na1; 2;  YOU Bi\|long3;  LIU Yi3;  CHENG Jian1; 2;  YUAN Jun1; 2
1.Hubei Key Laboratory of Novel Chemical Reactor and Green Chemical Technology, Wuhan Institute of Technology,
Wuhan 430074, China;2.Key Laboratory for Green Chemical Process of Ministry of Education, Wuhan Institute of
Technology, Wuhan 430074, China;3.China Petroleum Chemical Industry Co., LTD Jingmen Branch, Jingmen 448000, China
关键词:
润滑油精制体系;  腐蚀;  萃取; 环烷酸
Keywords:
lubricating oil refining device; corrosion; extract; naphthenic acid
分类号:
TE6263
DOI:
-
文献标志码:
AAdoi:103969/jissn16742869201204002
摘要:
为了探究生产润滑油的原料油品中引起精制装置腐蚀的重要物质因素，对润滑油精制装置的原料油品进行分析。首先将原料油品中活性组分用氢氧化钠\|乙醇溶液萃取出来，再对原料油品及萃取后的油样进行腐蚀实验，并用红外光谱分析萃取前后原料油品性质的变化以及活性组分的物质组成。结果表明：装置的腐蚀是由原料油品中活性组分引起的，且腐蚀只在较高温度下进行。经过与环烷酸、糠酸的红外谱图对照，证明造成装置腐蚀的活性组分是环烷酸类。
Abstract:
In order to find out the material caused serious corrosion in the operation of lubricating oil refining device, the raw oil of refining unit was analyzed. Firstly, the active component was extracted with sodium hydroxide\|ethanol solution from the raw oil, then corrosion experiment was proceeded, and infrared spectrum was used to detect the change of properties between raw oil with the active component before and after extracted and the composition of the active component. The result shows that the active component is demonstrated the main material causing the serious corrosion only at high temperature. By comparing infrared spectrum with furfural acid and the naphthenic acid, the active component is proved the naphthenic acid.

参考文献/References:

［1］高延敏，陈家坚，霄良才，等环烷酸腐蚀研究现状和防护对策［J］石油化工腐蚀与防护，2000，17（2）：6-11
［2］宋昭峥，侯永宾，王晓琳我国润滑油生产存在的问题及发展战略［J］润滑油与燃料，2009，19（1/2）：1-5
［3］徐祗宏，李勇润滑油糠醛精制装置设备的腐蚀与防护［J］石油化工腐蚀与防护，2003，20（3）：9-12.
［4］金南燕润滑油糠醛精制装置设备的腐蚀与防护［J］石油化工安全环保技术，2010，26（1）：1-4
［5］任翠霞原油中环烷酸腐蚀机理及防腐蚀措施［J］石油化工腐蚀与防护，2009，26（Z）：39-41
［6］吕振波，田松柏，翟玉春，等原油中环烷酸腐蚀预测方法综述［J］石油化工腐蚀预防护，2004，21(3)：1-4
［7］梁春雷，陈学东，艾志斌，等环烷酸腐蚀机理及其影响因素研究综述［J］．压力容器，2000，25（5）：30-36
［8］李美蓉，马济飞，孙向东超稠油中酸性组分的分离及其表面活性研究［J］石油化工高等学校学报，2006，19（3）：60-63
［9］李晓波，李之平 克拉玛依原油中活性组分的分离与分析［J］油田化学，1999，16（4）：333-335
［10］Piehl R L．Naphthenic acid corrosion in crude distillation units［J］Corrosion，1987，25(6)：196-201．
［11］Lee H，Wood L K．Naphthenic acid corrosion in a refinery setting［J］ Corrosion,1993，33(9)：631-640.