[1]吴江渝,李竹,胡易然,等.纳米金/琼脂糖复合凝胶制备及其催化性能[J].武汉工程大学学报,2014,(09):42-48.[doi:103969/jissn16742869201409009]
　WU Jiang yu,LI Zhu,HU Yi ran,et al.Preparation and catalytic property of gold nanoparticlesagarose gel[J].Journal of Wuhan Institute of Technology,2014,(09):42-48.[doi:103969/jissn16742869201409009]
点击复制

纳米金/琼脂糖复合凝胶制备及其催化性能(/HTML)
分享到：

《武汉工程大学学报》[ISSN:1674-2869/CN:42-1779/TQ]

卷:
期数:
2014年09期
页码:
42-48
栏目:
化学与化学工程
出版日期:
2014-09-30

文章信息/Info

Title:
Preparation and catalytic property of gold nanoparticlesagarose gel
文章编号:
16742869(2014)09004207
作者:
吴江渝; 李竹; 胡易然; 许谦
武汉工程大学材料科学与工程学院，湖北 武汉430074
Author(s):
WU Jiangyu;  LI Zhu;  HU Yiran;  XU Qian
School of Material Science and Engineering，Wuhan Institute of Technology，Wuhan 430074，China
关键词:
琼脂糖; 纳米金粒子; 复合凝胶; 对硝基苯酚; 催化剂
Keywords:
agarose;  gold nanoparticle;  composite gel;  pnitrophenol;  catalyst
分类号:
O614.123
DOI:
103969/jissn16742869201409009
文献标志码:
A
摘要:
以琼脂糖作为模板、稳定剂和还原剂，通过一步法合成了纳米金粒子及纳米金/琼脂糖复合凝胶，对纳米金粒子进行了表征，并以对硝基苯酚催化还原为模型反应研究了纳米金/琼脂糖复合凝胶的催化性能.结果表明，纳米金粒子为球状，粒径为1~10 nm，分布较均一；纳米金/琼脂糖复合凝胶表现出明显的催化活性，在实验条件下完全反应时间约为30 min.在重复利用实验中，该复合凝胶的催化性能随使用次数增多有一定下降.通过琼脂糖和氯金酸一步法制备纳米金/琼脂糖复合凝胶，方法简单、使用方便、后处理容易，为新型纳米金属催化剂的设计、合成及应用提供了新的思路.
Abstract:
Gold nanoparticles and nanogold/agarose composite gel were prepared in a onestep process using agarose as template, stabilizer and reducing agent. The gold nanoparticles were characterized and the catalytic activity of the composite gel was investigated using the reduction of pnitrophenol as the model reaction. The result shows that the majority of gold nanoparticles are spherical with 110 nm in diameter and distributed evenly; the nanogold/agarose composite gel shows good catalytic activity and the reaction finishes in 30 min in experimental conditions, but the catalytic activity of the composite gel declines in recycling assay. It indicates that the preparation of nanogold/agarose composite gel has advantages of facile synthesis, easy handling and convenient recycling, which provides a new way for design, synthesis and application of metal nanocatalysts.

参考文献/References:

［1］MURPHY C J. Nanocubes and nanoboxes［J］. Science, 2002, 298(5601): 21392141［2］CARLSON M T, GREEN A J, RICHARDSON H H. Superheating water by CW excitation of gold nanodots［J］. Nano Letters, 2012, 12(3): 15341537.［3］VIGDERMAN L, KHANAL B P, ZUBAREV E R. Functional gold nanorods: synthesis, self‐assembly, and sensing applications［J］. Advanced Materials, 2012, 24(36): 48114841.［4］LIU Q, LAI L, HUANG H, et al. Highyield synthesis of branched gold nanocrystals by a sodium diphenylamine4sulfonate reduction process in polyethylene glycol aqueous solution［J］. Chinese Journal of Chemistry, 2010, 28(4): 537542.［5］SREEPRASAD T S, SAMAL A K, PRADEEP T. Bodyor tipcontrolled reactivity of gold nanorods and their conversion to particles through other anisotropic structures［J］. Langmuir, 2007, 23(18): 94639471. ［6］XIAO J, QI L. Surfactantassisted, shapecontrolled synthesis of gold nanocrystals［J］. Nanoscale, 2011, 3(4): 13831396.［7］周旭, 吴江渝, 李妍. 三向聚酰胺胺树形分子模板法制备纳米金［J］. 武汉工程大学学报, 2010, 32(7): 7477.ZHOU X, WU J Y, LI Y. Preparation of gold nanocluster using threedirection PAMAM dendrimer as template［J］. Journal of Wuhan Institute Technology，2010, 32(7): 7477.(in Chinese)［8］党婕, 艾媛媛, 郑行望. 壳聚糖/PEI 凝胶模板法制备 Au/SiO2 复合纳米粒子［J］. 陕西师范大学学报：自然科学版, 2014, 42(1):5661.DANG J, AI Y Y, ZHENG X W. The synthesis of Au/SiO2 nanocomposites using chitosan/ PE composite nanohydrogel as template［J］. Journal of Shaanxi Normal University：Natural Science Edition, 2014, 42(1):5661.(in Chinese).［9］ABDELRASOUL G N, CINGOLANI R, DIASPRO A, et al. Photochemical synthesis: Effect of UV irradiation on gold nanorods morphology［J］. Journal of Photochemistry and Photobiology A: Chemistry, 2014, 275: 711.［10］杨立平, 涂伟霞. 微波法合成纳米金胶体颗粒的调控研究［J］. 物理化学学报, 2006, 22(4): 513516.YANG L P, TU W X. Studies on Au colloidal nanoparticles synthesized by microwave irradiation［J］. Acta PhysicoChimica Sinica, 2006, 22(4): 513516.(in Chinese)［11］沈理明, 姚建林, 顾仁敖. 金纳米粒子的电化学合成及光谱表征［J］. 光谱学与光谱分析, 2006, 25(12): 19982001.SHEN L M, YAO J L, GU R A. Electrochemical synthesis and spectroscopic characterization of gold nanoparticles［J］. Spectroscopy and Spectral Analysis, 2006, 25(12): 19982001.(in Chinese)［12］李兰芳, 杨平, 宋宏图, 等. 纳米金/4, 4′二巯基二苯硫醚自组装膜修饰金电极的制备及其电化学行为研究［J］. 武汉工程大学学报, 2011, 32(12): 69.LI L F, YANG P, SONG H T, et al. Electrochemical behavior of gold nanoparticles and 4, 4cDimercaptodiphenyl sulfide ether selfassembled monolayer modified gold electrode and its analytical application［J］. Journal of Wuhan Institute Technology, 2011, 32(12): 69.(in Chinese)［13］张帆, 齐文杰, 安学勤, 等. 反相微乳液中纳米金的可控合成及其机理研究［J］. 稀有金属材料与工程, 2012, 40(11): 20552059.ZHANG F, QI W J, AN X Q, et al. Controlled synthesis and mechanism of gold nanoparticles in reverse microemulsions［J］. Rare Metal Materials and Engineering, 2012, 40(11): 20552059.(in Chinese)［14］周海英, 周瑞, 熊斌, 等. 大长径比金纳米棒的合成及其单细胞毒性研究［J］. 分析化学, 2013, 40(12): 18071815.ZHOU H Y, ZHOU R, XIONG B, et al. Preparation and cytotoxicity of highaspectratio gold nanorods at single cell level［J］. Chinese Journal of Analytical Chemistry, 2013, 40(12): 18071815.(in Chinese)［15］MA Z, DAI S. Development of novel supported gold catalysts: A materials perspective［J］. Nano Research, 2011, 4(1): 332.［16］LOPEZACEVEDO O, KACPRZAK K A, Akola J, et al. Quantum size effects in ambient CO oxidation catalysed by ligandprotected gold clusters［J］. Nature Chemistry, 2010, 2(4): 329334.［17］KUDO S, MAKI T, FUKUDA T, et al. Prereduction of Au/Iron oxide catalyst for lowtemperature watergas shift reaction below 150 ℃［J］. Catalysts, 2011, 1(1): 175190.［18］ZOPE B N, HIBBITTS D D, NEUROCK M, et al. Reactivity of the gold/water interface during selective oxidation catalysis［J］. Science, 2010, 330(6000): 7478.［19］BU W, ZHAO L, ZHANG Z, et al. Effect of water on hydrogenation of 1, 3butadiene over Au (111): A joint theoretical and experimental study［J］. Applied Surface Science, 2014, 289: 613.［20］KIITTISAKMONTREE P, PONGTHAWORNSAKUN B, YOSHIDA H, et al. The liquidphase hydrogenation of 1heptyne over PdAu/TiO2 catalysts prepared by the combination of incipient wetness impregnation and depositionprecipitation［J］. Journal of Catalysis, 2013, 297: 155164.［21］GUACCIO A, BORSELLI C, OLIVIERO O, et al. Oxygen consumption of chondrocytes in agarose and collagen gels: a comparative analysis［J］. Biomaterials, 2008, 29(10): 14841493.［22］POTOCZEK M, ZIMA A, PASZKIEWICZ Z, et al. Manufacturing of highly porous calcium phosphate bioceramics via gelcasting using agarose［J］. Ceramics International, 2009, 35(6): 22492254. ［23］MA X, XIA Y, NI L, et al. Preparation of gold nanoparticlesagarose gel composite and its application in SERS detection［J］. Spectrochimica Acta Part A: Molecular and Biomolecular Spectroscopy, 2014, 121: 657661.［24］WANG X, EGAN C E, ZHOU M, et al. Effective gel for gold nanoparticle formation, support and metal oxide templating［J］. Chemical Communications, 2007 (29): 30603062.

相似文献/References:

[1]王璀璨,陈常连*,黄小雨,等.琼脂糖凝胶注模成型3Y-ZrO2的制备及表征[J].武汉工程大学学报,2017,39(01):59.[doi:10. 3969/j. issn. 1674?2869. 2017. 01. 010]
　WANG Cuican,CHEN Changlian*,HUANG Xiaoyu,et al.Preparation and Characterization of Gel-Casting 3Y-ZrO2 Using Agarose[J].Journal of Wuhan Institute of Technology,2017,39(09):59.[doi:10. 3969/j. issn. 1674?2869. 2017. 01. 010]
[2]杨　婉,王映桂,孙　鹏,等.琼脂糖凝胶中树枝状银的生长研究[J].武汉工程大学学报,2017,39(03):248.[doi:10. 3969/j. issn. 1674?2869. 2017. 03. 008]
　Controlled Growth of Silver Dendrites in Agarose Gel.Controlled Growth of Silver Dendrites in Agarose Gel[J].Journal of Wuhan Institute of Technology,2017,39(09):248.[doi:10. 3969/j. issn. 1674?2869. 2017. 03. 008]

备注/Memo

备注/Memo:
收稿日期：20140731基金项目：国家自然科学基金项目（51003081）作者简介：吴江渝（1977），男，广东电白人，教授，博士.研究方向：树形分子、聚丙烯酸合成及应用、纳米功能材料合成及应用.
更新日期/Last Update: 2014-10-10