|本期目录/Table of Contents|

[1]池汝安,石玉磬,陈志伟,等.盐酸对冶金污泥中铜锌镉铅的浸出工艺优化[J].武汉工程大学学报,2013,(05):1-5.[doi:103969/jissn16742869201305001]
　CHI Ru an,SHI Yu qing,CHEN Zhi Wei,et al.Extract technology of heavy metals from metallurgical sludge byhydrochloric acid[J].Journal of Wuhan Institute of Technology,2013,(05):1-5.[doi:103969/jissn16742869201305001]
点击复制

盐酸对冶金污泥中铜锌镉铅的浸出工艺优化(/HTML)
分享到：

《武汉工程大学学报》[ISSN:1674-2869/CN:42-1779/TQ]

卷:
期数:
2013年05期
页码:
1-5
栏目:
化学与化学工程
出版日期:
2013-05-31

文章信息/Info

Title:
Extract technology of heavy metals from metallurgical sludge byhydrochloric acid
文章编号:
16742869(2013)05000105
作者:
池汝安; 石玉磬; 陈志伟; 余军霞
武汉工程大学化工制药学院，绿色化工过程教育部重点实验室，湖北 武汉 430074
Author(s):
CHI Ruan;  SHI Yuqing;  CHEN ZhiWei;  YU Junxia
Key Laboratory for Green Chemical process of Ministry of Education, School of chemical Engineering and Pharmacy, Wuhan Institate of Technology,Wuhan 430074, China
关键词:
冶金污泥; 酸浸; 浸出率; 单因素实验
Keywords:
metallurgical sludge;  acid leaching;  leach rate;  single factor experiment
分类号:
TF81
DOI:
103969/jissn16742869201305001
文献标志码:
A
摘要:
为了能够充分回收利用冶金污泥中的有价金属，采用盐酸作为浸取剂浸出污泥中的重金属，并进行浸出工艺的优化.首先对污泥性质进行分析，分别采用烘干法测定冶金污泥的含水率，用X射线荧光光谱仪测定试样中金属成分及质量分数，用X射线衍射仪对试样中各元素的物相特征进行定性和定量分析.结果显示：污泥含水率为75.88%；干污泥含铜和锌的质量分数分别是1.51%和1.71%；污泥矿物相中铜主要以单质形式存在，锌主要以闪锌矿形式存在.然后采用盐酸作浸取剂，在单因素条件下进行浸出反应.研究了冶金污泥中铜、锌、镉、铅等重金属的浸出规律，并考察了浸出温度、浸出时间、盐酸浓度、液固比、粒径等因素对浸出率的影响.盐酸浸出污泥中重金属最佳工艺参数：浸出温度为25 ℃，浸出时间为10 min，盐酸浓度为1 mol/L，液固比为25∶1（mL/g），干污泥粒度小于150 μm.在此条件下，铜、锌、镉、铅的浸出率可分别达到84.4%、88.1%、98.8%、85.4%.盐酸浸出最佳工艺条件的确定，对工业应用有一定实用价值.
Abstract:
Hydrochloric acid was using as leaching agent to extract heavy metals from metallurgical sludge, and extract technology was optimized to recycle heavy metals from sludge. Moisture content of the sludge was determined by drying method. Metal component and mass fraction were determined by Xray fluorescence spectrometer. Phase characteristics of each element were analyzed by Xray diffraction. The analysis results show that moisture content metallurgical sludge is 75.88% of, mass fractions of copper and zinc are 1.51% and 1.71% in dry sludge, respectively. Copper exists in the form of simple substance, and zinc mainly exists in the form of sphalerite. Hydrochloric acid leaching process was studied to leach heavy metals such as copper, zinc, cadmium, lead from metallurgical sludge. Parameters such as leaching temperature, leaching time, concentration of hydrochloric acid, and grain diameter were investigated. The optimum results are 25 ℃ of leaching temperature, 10 minutes of leaching time, 1 mol/L of concentration of hydrochloric acid, 25∶1(mL/g) of liquidsolid ratio and less than 150 μm of grain diameter. The recovery of copper, zinc, cadmium, lead is 84.4%, 88.1%, 98.8%, 85.4%, respectively. The above investigation is valuable for industrial applications of leaching technology by hydrochloric acid.

参考文献/References:

［1］邹照华, 何素芳, 韩彩芸, 等. 重金属废水处理技术研究进展\[J\]. 水处理技术, 2010, 36(6): 1721. ZOU Zhaohua, HE Sufang, HAN Caiyun, et al. Progress of heavy metals liquid waste processing technique\[J\]. Technology of Water Treatment, 2010, 36(6):1721. (in Chinese)［2］JEOUNG J. Solidification/stabilization of Gredged Sludge with Low Alkalinity Additives and Geoenviromental Assessment\[M\]. Kyoto: Kyoto University, 2003.［3］郑喜珅, 鲁安怀, 高翔, 等. 土壤中重金属污染现状与防治方法\[J\]. 土壤与环境, 2002, 11(1): 7984.ZHENG Xishen, LU Anhuai, GAO Xiang, et al. Contamination of heavy metals in soil present situation and method\[J\]. Soil and Environmental Sciences, 2002,11(1):7984. (in Chinese)［4］王继元. 电镀重金属污泥的水泥固化处理试验研究\[J\]. 化工时刊, 2006, 20(1): 4447.WANG Jiyuan. Research on cement solidification experiment of electroplation heavy metal sludge\[J\]. Chemical Industry Times, 2006, 20(1): 4447. (in Chinese)［5］DILEK F B, GOKCAY C F. Microbiology of activated sludge treating waste water containing Ni(II) and Cr(VI)\[J\]. Water Science and Technology, 1996, 34(5/6):183191.［6］刘燕. 电镀污泥的无害化处理及综合利用技术\[J\]. 化工设计通讯, 2007,33(2): 5660.LIU Yan. Harmless treatment and comprehensive utilization technigue of electroplating sludge\[J\]. Chemical Engineering Design Communications, 2007,33(2): 5660. (in Chinese)［7］陈永松, 周少奇. 电镀污泥的基本理化特性研究\[J\]. 中国资源综合利用, 2007, 25(5): 26.CHEN Yongsong, ZHOU Shaoqi. Study on physical and chemical properties of electroplating sludges\[J\]. China Resources Comprehensive Utilization, 2007, 25(5): 26. (in Chinese)［8］程洁红, 陈娴, 孔峰, 等. 氨浸加压氢还原法回收电镀污泥中的铜和镍\[J\]. 环境科学与技术, 2010, 33(6): 135137,140.CHENG Jiehong,CHEN Xian,KONG Feng, et al. Recovery of copper and nickel from electroplating sludge by ammonia leaching and hydrogen reduction under high pressure\[J\]. Environmental Science & Technology, 2010, 33(6): 135137,140. (in Chinese)［9］吴宝明, 赵浩, 张宇峰,等. 电镀污泥的处理和综合利用研究进展\[J\]. 安全与环境学报, 2004（4）:9598.WU Baoming, ZHAO Hao, ZHANG Yufeng, et al. Review of treatment and comprehensive utilization of electroplating sludge\[J\]. Journal of Safety and Environment, 2004（4）:9598. (in Chinese)［10］季文佳, 黄启飞, 王琪,等. 电镀污泥资源化与处置方法的研究\[J\]. 电镀与环保, 2011,30(1): 4245.JI Wenjia, HUANG Qifei, WANG Qi, et al. A study of methods for resourcization and disposal of electroplating sludge\[J\]. Electroplating & Pollution Control, 2011,30(1): 4245. (in Chinese)［11］ZHU Wanpeng, YANG Zhihua. The Metals Recovery from Electroplating Sludge Using Solvent Extraction\[J\]. Water & Waste Engineering, 1995(12): 1618.［12］SILVA J E, PAIVA A P, SOARES D, et al. Solvent Extraction Applied to the Recovery of Heavy Metals from Galvanic Sludge\[J\]. Journal of Hazardous Materials, 2005, 120(1/2/3): 113118.［13］LI Chuncheng, XIE Fengchun, MA Yang, et al. Recovery of Multiple Heavy Metals Extraction and Recovery from Hazardous Electroplating Sludge Waste via Ultrasonically Enhanced Twostage Acid Leaching\[J\]. Journal of Hazardous Materials, 2010, 178(1/2/3): 823833.［14］PAULA T S S, NIELSON T M, MARTA M M D, et al. Extracion and recovery of chromium from electroplating sludge\[J\]. Journal of Hazardous Materials, 2006, 128(1): 3943.［15］王吉坤,张博亚.铜阳极泥现代综合利用技术\[M\]. 北京：冶金工业出版社, 2008: 3465.WANG Jikun, ZHANG Boya. Copper Anode Mud Comprehensive Utilization of Modern Technology\[M\]. Beijing:Metallurgical Industry, 2008: 3465.(in Chinese)

相似文献/References:

[1]刘安,孙家寿*,李神勇.含磷电镀污泥制取磷铵的试验[J].武汉工程大学学报,2011,(02):49.[doi:10.3969/j.issn.16742869.2011.02.013]
　LIU An,SUN Jia shou,LI Shen yong.Study on preparation DAP from sludge in electroplating plant[J].Journal of Wuhan Institute of Technology,2011,(05):49.[doi:10.3969/j.issn.16742869.2011.02.013]
[2]关洪亮,张璐,祝雅杰,等.电镀污泥中铬的去除工艺优化[J].武汉工程大学学报,2013,(09):44.[doi:103969/jissn16742869201309009]
　GUAN Hong\|liang,ZHANG Lu,ZHU Ya\|jie,et al.Technical investigation of removing chromium in electroplating sludge[J].Journal of Wuhan Institute of Technology,2013,(05):44.[doi:103969/jissn16742869201309009]
[3]池汝安,石玉磬,余军霞,等.冶金污泥中铜锌镉铅的氨水和碳酸铵选择性浸出分离[J].武汉工程大学学报,2014,(02):1.
　Chi Ru-an,Chen Zhi-wei,Shi Yu-qing,et al.Selective leaching of Cu, Zn, Cd and Pb from metallurgical sludge by ammonia-ammonium salt[J].Journal of Wuhan Institute of Technology,2014,(05):1.
[4]池汝安,石玉磬,余军霞,等.冶金污泥中铜锌镉铅的氨水和碳酸铵选择性浸出分离[J].武汉工程大学学报,2014,(02):1.[doi:10.3969/j.issn.16742869.2014.02.001]
　CHI Ru an,SHI Yu qing,YU Jun xia,et al.Selective leaching of Cu,Zn,Cd and Pb from metallurgical sludge by ammoniaammonium salt[J].Journal of Wuhan Institute of Technology,2014,(05):1.[doi:10.3969/j.issn.16742869.2014.02.001]

备注/Memo

备注/Memo:
收稿日期：20130416基金项目：教育部长江学者和创新团队发展计划(IRT0974）作者简介：池汝安（1959），男，福建宁化人，教授，博士，博士研究生导师.研究方向:矿物加工、分离工程.第35卷第5期2013年05月武汉工程大学学报JWuhanInstTechVol35No5May2013
更新日期/Last Update: 2013-06-04