|本期目录/Table of Contents|

[1]高荣,金士威*,张旭,等.硫铁矿烧渣制备高铁酸钾及高铁酸钾溶液稳定性[J].武汉工程大学学报,2011,(11):38-42.
　GAO Rong,JIN Shi wei,ZHANG Xu,et al.Preparation of potassium ferrate with pyrite cinders andpotassium ferrate solution’s stability[J].Journal of Wuhan Institute of Technology,2011,(11):38-42.
点击复制

硫铁矿烧渣制备高铁酸钾及高铁酸钾溶液稳定性(/HTML)
分享到：

《武汉工程大学学报》[ISSN:1674-2869/CN:42-1779/TQ]

卷:
期数:
2011年11期
页码:
38-42
栏目:
化学与化学工程
出版日期:
2011-11-30

文章信息/Info

Title:
Preparation of potassium ferrate with pyrite cinders and
potassium ferrate solution’s stability
文章编号:
16742869(2011)11003805
作者:
高荣1; 金士威1*; 张旭1; 刚典臣2
1.武汉工程大学化工与制药学院，绿色化工过程教育部重点实验室，湖北 武汉 430074；
2.美国路易斯安那大学拉法叶分校工程学院，路易斯安那州 拉斐特 70504
Author(s):
GAO Rong1; JIN Shiwei1; ZHANG Xu1; GANG Daniel Dianchen2
1.Key Laboratory of Green Chemical Process of Ministry of Education,
School of Chemical Engineering and Pharmacy,Wuhan Institute of Technology,Wuhan 430074,China;
2.College of Engineering，the University of Louisiana at Lafayette，Lafayette LA 70504，USA
关键词:
硫铁矿烧渣; 高铁酸钾; 次氯酸钠氧化法; 稳定剂
Keywords:
pyrite cinders; potassium ferrate; sodium hypochlorite oxidation; stabilizer
分类号:
TQ111.14
DOI:
-
文献标志码:
AAdoi:10.3969/j.issn.16742869.2011.11.010
摘要:
以硫铁矿烧渣为原料，采用酸解水浸法制备硫酸铁，并用次氯酸钠氧化法制备高铁酸钾.实验结果表明，硫铁矿烧渣制备硫酸铁溶液的最佳工艺条件为：水跟硫铁矿烧渣的质量比为0.65，质量分数为98%的浓硫酸酸解，在280 ℃下酸解反应1 h，铁的回收率可达78.6%；合成高铁酸钾最佳工艺条件为：在25 ℃时，次氯酸钠质量分数20%，硫酸铁跟氢氧化钠的质量比为0.65，反应时间1.5 h，高铁酸钾的产率可达到73.4%；高铁酸钾溶液最佳的储存方法为：聚乙烯塑料瓶避光保存，并添加稳定剂NaIO4，NaIO4在高铁酸钾溶液中的适宜质量分数为0.10%.
Abstract:
Ferric sulfate was prepared using pyrite cinders as raw material by acid splittingwater extraction method.Then potassium ferrate was produced with ferric sulfate by sodium hypochlorite oxidation method.The results of the preparation of ferric sulfate solution from pyrite cinders showed that the best operation conditions as follows:Under the condition of the weight ratio of water and pyrite cinder was 0.65 and 98% sulfuric acid for acid splitting,the recovery rate of ferrum was 78.6% after reacting 1 hour at 280 ℃.Moreover,the best operation conditions of producing potassium ferrate demonstrated as follows：with 20% of the sodium hypochlorite and 0.65 of the mass ratio between ferric sulfate and sodium hydroxide by weight,the yield of potassium ferrate can reach 73.4% by reacting 1.5 hours at 25 ℃.The best storage way was that avoided light and mixed with 0.10% of NaIO4 as stabilizer in polyethylene plastic bottles.

参考文献/References:

［1］刘青花，陈金芳，张良均.硫铁矿烧渣提取氧化铁红的研究［J］.武汉化工学院学报，2005，27(2)：13.
［2］张嵩松，冯启明.硫铁矿烧渣湿法制备铁红的简易工艺研究［J］.现代涂料与涂装，2007，10(12)：4345.
［3］王守庆，刘春华，魏怀生，等．硫铁矿烧渣的综合利用［J］．天津化工，2003(7)：2931．
［4］Li C，Li X Z L.A study of the preparation and reactivity of potassium ferrate［J］．Chemosphere，2005，61：537543.
［5］Ciabatti I，F Tognotti L.Treatment and reuse of dyeing effluents by potassium ferrate［J］．Lombardi Desalination,2010，250(1)：222228.
［6］苑宝玲，李坤林，邓临莉，等．多功能高铁酸盐去除饮用水中砷的研究［J］．环境科学学报，2006，27(2)：281284.
［7］贺素姣.高铁酸钾的制备与测定研究进展［J］．化工技术与开发，2010，39(11）：3942.
［8］杜建，梁桓国，张选峰，等．多功能水处理剂的应用研究进展［J］．环保科技，2010，16(1)：2628．
［9］徐颖惠，林维晟，刘俊劭，等．酸解法回收硫铁矿烧渣中铁的研究［J］．化学工程与装备,2008(9）：32.
［10］张莉，刘玉娟，丁瑶，等.硫酸亚铁制备高铁酸钾的工艺［J］.武汉工程大学学报，2011，33(1)：3234.
［11］王海舟．铁矿石分析［M］．北京：科学出版社，2000：166189.
［12］贾汉东，杨新玲，杨勇．高铁酸盐的直接分光光度法测定［J］．分析化学，1999，27(4)：617．

相似文献/References:

[1]张莉,刘玉娟,丁瑶,等.硫酸亚铁制备高铁酸钾的工艺[J].武汉工程大学学报,2011,(01):32.[doi:10.3969/j.issn.16742869.2011.01.009]
　ZHANG Li,LIU Yiu juan,DING Yao,et al.Research on synthesis of potassium ferrate using ferrous sulfate[J].Journal of Wuhan Institute of Technology,2011,(11):32.[doi:10.3969/j.issn.16742869.2011.01.009]

备注/Memo

备注/Memo:
-
更新日期/Last Update: