文章信息/Info

Title:
Preparation and its structure characterization of high porous density anodized aluminum oxide template
文章编号:
10044736(2008)01004803
作者:
王学华1; 马连姣1; 许震1; 曹宏1; 张保华2
1.武汉工程大学材料科学与工程学院，武汉 430074;
2.武汉工程大学分析测试中心，武汉 430074
Author(s):
WANG Xuehua1;  MA Lianjiao1;  XU Zhen1;  CAO Hong1;  ZHANG Baohua2
1.School of Materials Science Engineering, Wuhan Institute of Technology, Wuhan 430074,China;
2. Center of Analysis and Measurement, Wuhan Institute of Technology, Wuhan, 430074,China
关键词:
多孔氧化铝; 双面多孔阳极氧化铝模板; 通孔
Keywords:
porous anodized aluminum oxide; AAO template; throughhole
分类号:
TG 146.1
DOI:
-
文献标志码:
A
摘要:
采用两步氧化法制备出双面多孔阳极氧化铝模板（AAO），并进一步发展了模板通孔工艺，得到单层高密度多孔氧化铝模板，并用XRD、SEM和AFM对模板结构进行了表征.结果表明， 草酸环境下制备的AAO模板孔排列高度规整，孔密度为1011个/cm2 量级，孔径为45~55 nm，孔间距为100~120 nm.
Abstract:
Doubleside porous anodized aluminum oxide (AAO) template was prepared by using twostep anodization and the process of thoughhole was developed, by which singleside thoughhole AAO template was fabricated. The microstructure of the AAO template was characterized by XRD, SEM and AFM. The result indicated that AAO with highordered hole array from oxalic acid condition has the hole density of 1011/cm2, hole diameter of 45~55 nm and distance between every two holes of 100~120 nm range.

参考文献/References:

［1］黎樵焱．铝阳极氧化膜形态结构和成分分布的研究［J］．表面技术，1992，21（4）：159.
［2］任刚，陈皓明．多孔型阳极氧化铝膜在纳米结构制备方面的研究和进展［J］．材料导报，2002，16（10）：4548.
［3］Huixin He, Nongjian J Tao. Electrochemical Fabrication of Metal Nanowires, Encyclopedia of Nanoscience and Nanotechnology［J］.USA:American Scintific Publishers, 2003,10:118.
［4］Itoh N, Kato K, Tsuji T,et al. Preparation of a tubular anodic aluminum oxide membrane［J］. Journal of Membrane Science, 1996, 117:189196.
［5］徐金霞，黄新民．二次阳极氧化方法制备有序多孔氧化铝膜［J］．化学物理学报，2003，16（3）：223226.
［6］Govyadinov A, Emeliantchik I, Kurilin A.Anodic aluminum oxide microchannel plates，Nuclear Instruments and Methods in Physics Research A, 1998, 419: 667675.
［7］Sauer G, Brehm G, Schneider S,et al. Highly ordered monocrystalline silver nanowire arrays［J］.JOURNAL OF APPLIED PHYSICS,2005,91(5):32433247.
［8］Vrublevsky I, Parkoun V, Schreckenbach J.Analysis of porous oxide film growth on aluminum in phosphoric acid using reanodizing technique［J］.Applied Surface Science, 2005，242:333338.

相似文献/References:

备注/Memo

备注/Memo:
收稿日期：20060719
基金项目：武汉市青年科技晨光计划（No.2006500411635）
作者简介：王学华（1976），男，湖北襄樊人，博士，副教授；
研究方向：纳米薄膜材料.
更新日期/Last Update: